Galvanized coil

Galvanized sheet

- Product name: Galvanized sheet
INQUIRY EMAIL

Product Introduction of Coating Business Division
Color Coated Sheet:
It is made by taking hot galvanized sheet and zinc-iron alloy hot galvanized sheet as the substrate through surface pretreatment, coating one or more layers of liquid coating by roll coating, baking and cooling. The used coatings including polyester, silicon modified polyester, high-durability polyester, polyvinylidene fluoride, epoxy and high corrosion-resisting coating are widely used for building, transport, home appliances, solar energy, furniture, etc. It is mainly used as the side door plate of refrigerators, and shell of DVDs, air conditionings, freezers, and washing machines.
Galvanized Sheet:
Hot galvanized sheet and alloying galvanized sheet have excellent performance, ideal combination property including corrosion resistance, formation and coating, and are mainly used for building, automobiles, metallurgy, and electrical equipment. Galvanized sheet is mainly used for making roof, door and window, roller shutter door, and suspended skeleton in building industry, vehicle shell, chassis, door, trunk lid, oil tank and fender in auto industry, steel sash blank and color coated sheet substrate in metallurgy industry, and refrigerator base, shell, refrigerating chamber, kitchen equipment and other parts in electrical equipment industry.
Cold Rolled Sheet:
Cold sheet has excellent type and surface quality and mechanical property indexes meeting customer demands. It is widely used for galvanized substrate, home appliances, tubbing, automobile, building, enamel, and other industries.
Hot Rolling Pickling Steel Strip

1、Range and Production Capacity

Production line	Product thickness mm	Product width mm	Steel coil weight (t)	Steel coil inner diameter mm	Production capacity (10,000t/a)
Push-pull pickling unit	1.8-4.0	800-1,250	≤28	610	65
Continuous pickling unit	1.8-4.5	800-1,280	≤28	610	120

2. Number and Mechanical Property

No.	Tensile test
	Yield strength Rel (MPa)	Tensile strength Rm (MPa)	Percentage elongation after fracture A%
	Yield strength Rel (MPa)	Tensile strength Rm (MPa)	1.8～＜2.0	2.0～＜2.5	2.5～＜3.2	3.2～＜4.0	≥4.0
SPHC		≥270	≥29	≥30	≥31	≥32	≥32
SPHD		≥270	≥32	≥33	≥35	≥37	≥39
SPHE		≥270	≥33	≥35	≥37	≥39	≥41
SS330	≥205	330～430	≥26
SS400	≥245	400～510	≥21
SAPH310	≥
SAPH370	≥370	≥255	≥32
SAPH400	≥
SAPH440	≥
Notes: 1. The tensile test specified value in the table is suitable for longitudinal test piece. 2. Tensile test uses sample of L0=50mm, b=25mm, namely P14 sample in GB/T228. 3. Steel strip is delivered in the state of hot rolling.